Large-size Blocks for Glass-melting Furnaces
Large-size blocks are intended for laying of bottom and walls of glass-melting furnace.
Technical characteristics
Rate for grade | ||||
---|---|---|---|---|
ShSU-33 | ShSU-40 | МLS-62 | МКS-72 | |
GOST 7151-74 rev.1-3 | GOST 24704-2015 | |||
Mass fraction, %: Al2O3, minimum Fe2O3, maximum |
33 1,8 |
40 1,5 |
over 62 1,5 |
over 72 1,5 |
Compressive strength, N/mm², minimum | 25 | 35 | 25 | 30 |
Open porosity, %, maximum | 18 | 18 | 24 | 24 |
Residual variation of dimensions when heating, %, maximum at: 1400 °C 1450 °C 1500 °C 1600 °C |
0,4 - - - |
- 0,4 - - |
- - 0,4 - |
- - - 1,0 |
Apparent density, g/cm³, minimum | - | 2,20 | n/a | |
Temperature of initial softening, °C, minimum | - | 1450 | - | - |
Upon agreement with the consumer grinding of bricks is provided.
Limit deviations of item dimensions, mm
Dimensions | ||
---|---|---|
ShSU-33 | ShSU-40 | |
length a | ||
up to 600 mm | ±4 | ±7 |
1000 mm | ±6 | ±10 |
1200 mm | ±7 | ±12 |
1400 mm | ±8 | ±14 |
Width б | ±4 | ±7 |
Thickness в | ±4 | ±5 |
Form and dimensions
Item number | Dimensions, мм | Group of complexity | ||
---|---|---|---|---|
a | б | в | ||
1 | 1000 | 400 | 300 | 10 |
2 | 1000 | 300 | 300 | 10 |
3 | 1000 | 400 | 250 | 10 |
4 | 1000 | 300 | 250 | 9 |
5 | 1000 | 400 | 200 | 9 |
6 | 1000 | 300 | 200 | 9 |
7 | 600 | 400 | 300 | 9 |
8 | 600 | 300 | 300 | 9 |
9 | 600 | 400 | 250 | 9 |
10 | 600 | 300 | 250 | 8 |
11 | 500 | 400 | 300 | 9 |
12 | 500 | 300 | 300 | 8 |
13 | 500 | 400 | 250 | 8 |
14 | 500 | 300 | 250 | 8 |
15 | 400 | 300 | 300 | 8 |